UPS 19060 SG (SGUW) Epoxy Metal Repair

Rate this item
(0 votes)

 

Data Sheet and Application Guide

 

Product Description

 


Unique Polymer Systems Epoxy Metal Repair UPS 19060 SG (also  SGUW the underwater version) is specially packaged rapid curing synthetic metal repair compound for on site repairs to metal components such as leaking pipes, tanks,ducts,radiators etc.


Product Features

 

Simple to use,only requiring simple hand mixing to activate reaction between the concentrically packed components.

Designed for application by gloved hand, putty knife or spatula.

Can be applied to any damaged metal surface, plus glass,fibreglass and other composite surfaces.

Designed for rapid repairs tcracked casting, leaking pipes, tanks, flanges etc minimising down-time.

Exhibits excellent adhesion to correctly prepared metal surfaces.

General Application Steps

1. Remove oil, grease and loosely adhering deposits.

2. Abrade by appropriate means to create a coarse profile.

3. Apply Epoxy Metal Repair  UPS 19600 to the required thickness.

4. Allow to cure.
5. Visually inspect the system for defects.
6. Repair any defects.
7. Carry out machining as required.

 

Property  - Value

Colour  -  Grey

           Ratio   -   N/A, supplied ready for use
Drying & Cure times at 20°C (68°F)
         Useable life                   6 mins
         Initial Set                    15 mins
        Hard Dry for machining 30 mins
        Full Mechanical Cure              2 hours
Volume Solids                  100%
Volume Capacity      66cc (4 cu ins) per unit
Performance Data
      Flexural Strength                            23Mpa (3250 psi) (ASTM D695)
      Heat distortion temperature         40°C (96°F)(ASTM D648)
     Tensile Shear Adhesion         4.5 Mpa (650 psi ) on grit blasted steel
     Maximum Operating Temperature  120 C  (248 F) Dry-- 70 C (185 F ) Wet
     Shore D Hardness                            85 (ASTM D2240)
    Corrosion Resistance   5000 hours (ASTM B117)

TECHNICAL DATA SHEET

VIDEO GUIDE 1 - VIDEO GUIDE 2