UPS 18601/3/4/5 PRHT EMERGENCY PIPE REPAIR BANDAGE - HIGH TEMPERATURE is a high-performance, ultra-strong, rapid curing moisture activated (activation within 5 seconds) pipe repair bandage which has been specially engineered to seal leaking pipework instantly with very limited surface preparation (SSPC SP2 Hand Tool Cleaning or SP3 Power Tool Cleaning).
It is a single component polyurethane resin (over 52% resin content) impregnated knitted fiberglass (24-26 stiches per cm2) bandage which requires no specialist training or equipment to use. It provides instant results to leaking, damage and corroded pipework, and is extremely easy to use. It is able to withstand 450°C once fully cured.
Easy to apply, requiring no special tools, training or equipment.
Specially selected woven fibreglass fabric impregnated with a polyurethane resin, which is activated by immersion in water – Very high stich count and resin content
Temperature resistance up to 450°C and down to -20°C
Can be used on a wide variety of surfaces, including all metals and many types of plastics (PVC, Fibreglass, Concrete, Steel etc.,)
Instant leak sealing –
Ready for immediate service which provides long term protection
Ideal for repairing pipes operating at low pressures up to 450 psi
Designed for use for repairs up to 500mm diameter
Chemically resistant to a wide range of industrial chemicals
Outstanding adhesion to manually prepared surfaces
(SSPC SP2 Hand Tool Cleaning or SP3 Power Tool Cleaning)
Very moisture tolerant pipe repair bandage –
It will even cure underwater
Applications for UPS 1801/3/4 PRHT EMERGENCY PIPE REPAIR BANDAGE - HIGH TEMPERATURE include:
Suitable for pipe repairs in low pressure systems –
Up to 450psi
Repairing various leaks used within all types of industries – Marine, mining, industrial etc.,
No Specialist Tools Required
30 Minutes to
Full Cure
Ultra-High Temperature Resistance 450°C (842°F)
Cost Effect Solution
Bandage Size
UPS 1803 PRHT 50mm x 2.6m
UPS 1805 PRHT 100mm x 3.6m
Pipe Nominal Bore
>200mm (7 7/8”)
>400mm (15 ¾”)
These times will be doubled at 10°C (50°F) and halved at 30°C (86°F)
Initial Set -
5 mins
Useable Life -
2-3 mins
Flexural Strength
(Tested to ASTM D790)
32Mpa (4,640 psi)
Tensile Strength
(Tested to ASTM D6382)
19Mpa (2,740psi)
12.5 bar (180 psi)
12mm / ¼ inch thick repair
Shore D Hardness
(Tested to ASTM D2240)
82
Maximum Pressure
(Tested to ASTM D1599)
450psi
31.6 bar (450 psi)
25mm / 1 inch thick repair
Maximum heat 450°C (842°F)