UPS 908 MP METAL PRIMER is a solvent based epoxy primer, for use on steel and concrete surfaces as a long-term protector against corrosion.
Solvent based epoxy coating
10,000 hours corrosion resistance
Applied in 1 or 2 coats at 100-125 microns per coat
Suitable for all metallic surfaces
Cures at temperatures down to 5°C
Formally known as GP 120
Applications for UPS 908 MP METAL PRIMER include:
Cold water lines
Structural Steel
Pipework
External tank surfaces etc
Surface Preparation Manual | Mechanical | Abrasive Blast
Brush or Roller Applied
Cures at Temperatures Down to 5°C
Long Term Protection
Against Corrosion
Useable Life
2 hours @ 20°C (68°F)
Minimum Over-Coating Window
6 hours @ 20°C (68°F)
Hardness Shore D
(ASTM D2240)
80
Salt Fog Resistance
(ASTM B117)
10,000 Hours
Available Colours
Dark Grey
Maximum Over-Coating Window
36 hours @ 20°C (68°F)
Corrosion Resistance
(ASTM B117)
Minimum 5000 Hours
Tensile Shear Adhesion
(ASTM D1002)
(Abrasive Blasted Mild Steel with 75 micron profile)
195KG/cm²
(2770 psi)
Pack Sizes
5LTR | 20LTR
5 LTR (1.3 US Gallon) of fully mixed material will give the following coverage rates -
33m² at 150 microns
355ft² at 6mil
20 LTR (5.3 US Gallon) of fully mixed material will give the following coverage rates -
133m² at 250 microns
1430ft² at 6mil
Please note that the coverage rates quoted are theoretical and don't take into consideration the profile or condition of the surface being repaired
Chemical
(1) Sulphuric Acid
(2) Sodium Hydroxide
(3) Hydrocholric Acid
(4) Phosphoric Acid
Concentration
(1) 20%
(2) 35%
(3) 10%
(4) 25%
Temperature
(1) 40°C
(2) 40°C
(3) 40°C
(4) 40°C
Suitable for use in immersed conditions at temperature up to 40°C (104°F)
Resistant to dry heat up to 120°C (248°F) dependent on load